FEATURES

TYPICAL APPLICATIONS
• Mothballing and layup
• Shipping
• Protective coating
• Storage

METALS PROTECTED
• Brass
• Cadmium
• Cast Iron
• Steel
• Magnesium
• Lead-calcium alloy
• Zinc

TYPICAL PROPERTIES
Appearance                                         Beige/Tan Liquid
Film Type                                                Oily
Flash Point                                            295°F (146°C)
Shelf Life                                                  24 months @ 75°F (24°C)
Non-volatile Content                  90-98%
Theoretical Spread Rate       1,450-1,580 ft2/gal @ 1 mil(36-39 m2/l @ 25 microns)
Density                                                      0.91 kg/l
Salt Spray (ASTM B117)       100 hrs 

Humidity (ASTM D1748)      1000 hrs

APPLICATION 

Surface Preparation Substrate should be free of grease, oil, dirt, fingerprints, drawing compounds, rust inhibitors (except Cortec® approved), or any other surface contamination that could affect adhesion. For production line applications, use VpCI®- 440 or similar phosphatizing pre-treatment. For structural steel applications, Cortec® recommends a minimum of a NACE #3/SSPC-SP6 commercial blast clean. Consult Cortec® Technical Service and/or test system adhesion prior to full scale application. 

Note: Power agitate to a uniform consistency using a “squirrel cage” type mixer, hand-held drill mixer, or other equivalent method. VpCI®-369D can be applied by spray, roll, brush, or dip.

Cleanup 

Clean tools/equipment immediately after use with butyl acetate when paint is still wet. When dry, use butyl cellosolve or MEK. Follow mfg’s safety recommendations when using any solvent.

PACKAGING
VpCI-369D is available in 5 gallon (19 liter) pails, 55 gallon (208 liter) drums, totes, and bulk.